Polymerization System - Solution Polymerization
Catalyst - high-cis polybutadiene with neodymium catalys
Configuration - 97% cis 1,4 content minimum
Appearance - Non-staining, No foreign matter
Characteristics - high-cis content, good
abrasion resistance;low temperature rise
Application - high performance tires, conveyor belts ,footwear soles
Specification Values
Polymer Properties | minimum | maximum |
Mooney Viscosity,ML(1+4)100℃ | 38 | 48 |
Volatile Matter,% | --- | 0.50 |
Ash,% | --- | 0.30 |
Compound Mooney Viscosity,ML(1+4)100℃ | --- | 80 |
300% Modulus，MPa | 8.5 | 13.5 |
Tensile Strength ，MPa | 15.0 | --- |
Elongation，% | 360.0 | --- |
PE film and kraft paper bag packing for piece of rubber or CM2, net
weight :25.0±0.25kg/bag
Polymerization System - Solution Polymerization
Catalyst - high-cis polybutadiene with neodymium catalys
Configuration - 97% cis 1,4 content minimum
Appearance - Non-staining, No foreign matter
Characteristics - high-cis content, good
abrasion resistance;low temperature rise
Application - high performance tires, conveyor belts ,footwear soles
Specification Values
Polymer Properties | minimum | maximum |
Mooney Viscosity,ML(1+4)100℃ | 38 | 48 |
Volatile Matter,% | --- | 0.50 |
Ash,% | --- | 0.30 |
Compound Mooney Viscosity,ML(1+4)100℃ | --- | 80 |
300% Modulus，MPa | 8.5 | 13.5 |
Tensile Strength ，MPa | 15.0 | --- |
Elongation，% | 360.0 | --- |
PE film and kraft paper bag packing for piece of rubber or CM2, net
weight :25.0±0.25kg/bag