Polymerization System - Solution Polymerization
Catalyst - Ziegler Nickel Type
Configuration - 96% cis minimum
Stabilizer - Non-staining
Specific gravity - 0.91
Characteristics - High abrasion resistance, high resilience, good low temperature properties
Application - Tire, footwear, belt, golf ball and other industrial rubber products.
Specification Values
Polymer Properties | minimum | maximum | |
Mooney Viscosity,ML(1+4)100℃ | 41 | 49 | |
Volatile Matter,% | --- | 0.50 | |
Ash,% | --- | 0.20 | |
Compound Properties(Test formula ASTM D-3189;Cure at 145℃) | |||
Compound Mooney Viscosity,ML(1+4)100℃ | --- | 65 | |
Tensil Strengh , MPa 35min | 13.2 | --- | |
Elongation ,% 35min | 330 | --- | |
300% Modulus, MPa | 25min | 7.0 | 12.0 |
35min | 8.0 | 13.0 | |
50min | 8.0 | 13.0 | |
Test formula ,GB/T8660B | PHR |
BR9000 | 100.00 |
HAF Black (IRB8#) | 60.00 |
ASTM Type 103 Petroleum oil | 15.00 |
Zinc Oxide | 3.00 |
Stearic Acid | 2.00 |
TBBS | 0.90 |
Sulfur | 1.50 |
Total | 182.40 |
Package: PE film and kraft paper bag packing for piece of rubber in bulk or Mental Box
net weight :25.0±0.25kg/bag
Polymerization System - Solution Polymerization
Catalyst - Ziegler Nickel Type
Configuration - 96% cis minimum
Stabilizer - Non-staining
Specific gravity - 0.91
Characteristics - High abrasion resistance, high resilience, good low temperature properties
Application - Tire, footwear, belt, golf ball and other industrial rubber products.
Specification Values
Polymer Properties | minimum | maximum | |
Mooney Viscosity,ML(1+4)100℃ | 41 | 49 | |
Volatile Matter,% | --- | 0.50 | |
Ash,% | --- | 0.20 | |
Compound Properties(Test formula ASTM D-3189;Cure at 145℃) | |||
Compound Mooney Viscosity,ML(1+4)100℃ | --- | 65 | |
Tensil Strengh , MPa 35min | 13.2 | --- | |
Elongation ,% 35min | 330 | --- | |
300% Modulus, MPa | 25min | 7.0 | 12.0 |
35min | 8.0 | 13.0 | |
50min | 8.0 | 13.0 | |
Test formula ,GB/T8660B | PHR |
BR9000 | 100.00 |
HAF Black (IRB8#) | 60.00 |
ASTM Type 103 Petroleum oil | 15.00 |
Zinc Oxide | 3.00 |
Stearic Acid | 2.00 |
TBBS | 0.90 |
Sulfur | 1.50 |
Total | 182.40 |
Package: PE film and kraft paper bag packing for piece of rubber in bulk or Mental Box
net weight :25.0±0.25kg/bag