Brief introduction
A xanthogen-modified polychloroprene rubber with medium crystallizaion rate, good heat resistance and stability at elevated temperature, It is similar to Denka Neoprene type W and Denka’s M-40.
Color and Form: White or light yellow chips
Product description
Module at 500% elongation Mpa: | 1~5 |
Tensile strength Mpa: | ≥12 |
Ultimate elongation (%): | ≥700 |
Mooney viscosity ML(1+4)100℃: | 42~54 |
Mooney scorch MSt5 (Min): | ≥11 |
Mass fraction of volatiles (Wt.%): | ≤1.2 |
Mass fraction of ash (Wt.%): | ≤1.2 |
Packing:
Woven polypropylene lined-kraft paper bags with a release polyethylene
liner, 25kg net weight each.
Application:
For making various light-colored rubber products such as seals, dust cover,
rubber covered roller, lining, hose coating wires, cables, belts and pipes.
Storage life:
one year below 20 ℃ and half a year below 30 ℃ from the date of production.
Brief introduction
A xanthogen-modified polychloroprene rubber with medium crystallizaion rate, good heat resistance and stability at elevated temperature, It is similar to Denka Neoprene type W and Denka’s M-40.
Color and Form: White or light yellow chips
Product description
Module at 500% elongation Mpa: | 1~5 |
Tensile strength Mpa: | ≥12 |
Ultimate elongation (%): | ≥700 |
Mooney viscosity ML(1+4)100℃: | 42~54 |
Mooney scorch MSt5 (Min): | ≥11 |
Mass fraction of volatiles (Wt.%): | ≤1.2 |
Mass fraction of ash (Wt.%): | ≤1.2 |
Packing:
Woven polypropylene lined-kraft paper bags with a release polyethylene
liner, 25kg net weight each.
Application:
For making various light-colored rubber products such as seals, dust cover,
rubber covered roller, lining, hose coating wires, cables, belts and pipes.
Storage life:
one year below 20 ℃ and half a year below 30 ℃ from the date of production.